ASTM D3410
|
|
This test method determines the in-plane compressive properties of polymer matrix composite materials reinforced by high-modulus fibers.
|
ASTM D3518
|
|
This practice determines the in-plane shear response of polymer matrix composite materials reinforced by high-modulus fibers. The composite material form is limited to a continuous-fiber reinforced composite +45° laminate capable of being tension tested in the laminate chi-direction.
|
ASTM D3552
|
|
This test method covers the determination of the tensile properties of metal matrix composites reinforced by continuous and discontinuous high-modulus fibers. Nontraditional metal matrix composites as stated in also are covered in this test method.
|
| ASTM D5467 |
|
This test method covers the in-plane compressive properties of polymer matrix composite materials reinforced by high-modulus fibers in a sandwich beam configuration.
|
ASTM D5766
|
|
This test method determines the open hole tensile strength of multidirectional polymer matrix composite laminates reinforced by high-modulus fibers.
|
| ASTM D6641 |
|
This test method establishes a procedure for determining the compressive strength and stiffness properties of polymer matrix composite materials using a combined loading compression or comparable test fixture.
|
ASTM F1276
|
|
This test method provides a means of measuring the amount of creep relaxation of a laminated composite gasket material at a predetermined time after a compressive stress has been applied.
|
| BS 4370-4:1991 |
|
Methods of test for rigid cellular materials. Method 14. Determination of flexural properties.
|
BS 4443-7:1992
|
|
Methods of test for flexible cellular materials. Method 17. Determination of tear strength of flexible cellular material with an integral skin. Method 18.
|